Our particle boards are very versatile and can be used for all types of interior applications. We manufacture the best quality of plain and pre-laminated particle boards specially to suit your various requirements. Our Grade I boards are for exterior use and Grade II boards are for interior use. Our expertise and European technology enables us to cater to different size requirements for different clients. While the sophisticated impregnation line, together with our in-house resin manufacturing, makes our boards far superior than those available in the market. Our particle board conforms to BIS standards and bear the ECO MARK.
Available in custom size if bulk quantity
- Treated Kiln dried hardwood exceeding 650 kgs/CBM
- Interior and exterior both are available
- Weight having 22 kgs per sq.meter for 35 mm thickness
- Imported PVU resin is used
- Highly moisture resistant
- High quality imported PVC foil used for laminating
- Vacuum pressure treatment (VPT) with preservative chemicals
- Easy to clean and maintain
- Consistent quality
- Adherence to international standards
- Economical board sizes resulting in minimal wastage
- Excellent acoustic properties
- High bending strength
- Excellent machinability
- Saves both time and labour
- The widest spectrum of applications
- Free from warpage and peeling of laminates
- Easy-to-install
- Ready-to-use
| Sr. No | Properties | Unit | Plain Particle Boards IS : 3087 |
Pre-laminated Particle Boards IS : 12823 |
||
| Grade – II | Grade – I | Grade – II | Grade – I | |||
| 1 | Density | Kg/m3 | 500-900 | 500-900 | 500-900 | 500-900 |
| 2 | Density Variation | % | +/-10 | +/-10 | +/-10 | +/-10 |
| 3 | Moisture Content | % | 5 to 15 | 5 to 15 | 5 to 15 | 5 to 15 |
| 4 | Modulus Of Rupture Up to 20mm thickness Above 20mm thickness |
N/mm2 | 11 11 |
15 12.5 |
11 11 |
15 12.5 |
| 5 | Tensile Strength Perpendicular To Surface a) After cyclic test b) Accelerated water resistance test |
N/mm2 | 0.2 0.15 |
0.2 0.15 |
||
| 6 | Water Absorption 2 Hours 24 Hours |
% | 40 80 |
10 20 |
15 30 |
7 15 |
| 7 | Thickness Swelling, 2Hours Soaking, Thickness, Length, Width |
% | 12 0.5 0.5 |
8 0.5 0.5 |
8 | 5 |
| 8 | Swelling Due To Surface Absorption | % | 9 | 6 | ||
| 9 | Tensile Strength Perpendicular To Surface Up to 20mm thickness Above 20mm thickness |
N/mm2 | 0.3 0.3 |
0.45 0.40 |
0.3 0.3 |
0.45 0.40 |
| 10 | Screw Withdrawal Strength Face Edge |
N | 1250 700 |
1250 850 |
1250 750 |
1250 800 |
| 11 | Abrasion Resistance 1) Type I 2) Type II 3) Type III |
Revolution | 450 250 80 |
450 250 80 |
||