Our decorative laminates are an integral part of India’s furniture industry. Used by being pasted on to any furniture made with plywood, plain particleboard and MDF, they impart great looking finishes and heighten the aesthic value of the furniture. The advantage of the laminates is that any colour and design combination can be used to create exactly what you’ve dreamed of. This freedom from design constraints makes it the first choice of those who are looking to renovate their lives.
Plymax decorative laminates are made by giving a hard base to lamination papers with melamine resin and thereby increasing life of the paper which in turn safeguard the colour and brightness of the paper.
Combined with an enviable abrasion resistance, our decorative laminates ensure long durability to the life of the colour.
Indigenous world standard machinery to ensure world-class quality
Manufactured with specially formulated in-house resins Introduces new and vibrant special shades to the market
The unique technology with strong in-house R & D makes ASIS LAM a superior product in design, finish, range, variety and quality
Plymax Lam conforms to Indian and International Standards
Special formulation assures for long-term use that retains the original gloss and colour
Durability with extra power and strength to resist abrasion
Carpenter friendly due to uniform, well-sanded back surface made by an imported sander machine that ensures better adherence of adhesive and more efficient use of glue
| Properties | As per IS: 2046 – 1995 (1 mm) | ASIS lam (1 mm) | As per IS: 2046 – 1995 (1.5 mm) | ASIS lam (1.5 mm) |
| Thickness (in mm) | 1.0 mm (+/- 0.1mm) | 1.0 mm (+/- 0.05mm) | 1.5 mm (+/- 0.1mm) | 1.5 mm (+/- 0.05mm) |
| Resistance to surface wear | >350 (revolutions) | > 400 | >350 (revolutions) | > 400 |
| Resistance to surface in boiling water Mass increase Thickness increase |
10.0 % (Max.) 11.8 % (Max.) |
6.0 7.0 |
7.5 % (Max.) 8.5 % (Max.) |
5.5 7.0 |
| Resistance to dry heat 180 degrees C | Should pass test | Complies | Should pass test | Complies |
| Dimentional stability at deviated temperature Longitude Transverse |
0.55 % (Max.) 1.025 % (Max.) |
0.35 0.75 |
0.44 % 0.86 % |
0.30 0.65 |
| Dimentional stability at 20 degrees C Longitude Transverse |
0.375 % (Max.) 0.60 % (Max.) |
0.275 0.48 |
0.31 % (Max.) 0.49 % (Max.) |
0.23 0.38 |
| Resistance to impact by small diameter ball | 20N (Min.) | 25N | 20N (Min.) | 30N |
| Resistance to cracking | Should pass test | Complies | Should pass test | Complies |
| Resistance to scratching | 2N (Min.) | 3N | 2.N (Min.) | 3.5N |
| Resistance to staining | Should pass test | Complies | Should pass test | Complies |
| Resistance to colour change 1. In Xenon light 2. In Enclosed Carbon ARC light |
Wool Standard 6 5 |
6 5 |
Wool Standard 6 5 |
6 5 |
| Resistance to cigarette burns | 3 | 3 | 3 | 3 |
| Resistance to steam | 4 | 4 | 4 | 4 |
| Appearance | Free from surface defects | Complies | Free from surface defects | Complies |
| Specific gravity gm/cm3 | NA | 1.36 (Min.) | NA | 1.4 (Min.) |
| Properties | As per IS: 2046 – 1995 (0.8 mm) |
ASIS Prime lam (0.8 mm) | As per IS: 2046 – 1995 Postforming Grade (0.6 mm) |
ASIS Flexi lam PF (0.6 mm) |
| Thickness (in mm) | 0.8 mm (+/- 0.1mm) | 0.8 mm (+/- 0.05mm) | 0.6 mm (+/- 0.1mm) | 0.6 mm (+/- 0.05mm) |
| Resistance to surface wear | 350 (revolutions) | > 350 | 350 (revolutions) | > 350 |
| Resistance to surface in boiling water Mass increase Thickness increase |
12.0 % (Max.) 14.0 % (Max.) |
<8.0 <9.0 |
22.0 % (Max.) 24 % (Max.) |
6.5 % 8.0 % |
| Resistance to dry heat 180 degrees C | Should pass test | Complies | Should pass test | Complies |
| Dimentional stability at deviated temperature Longitude Transverse |
0.625 % (Max.) 1.10 % (Max.) |
<0.45 <0.70 |
0.75 % (Max.) 1.25 % (Max.) |
0.35 % 0.75 % |
| Dimentional stability at 20 degrees C Longitude Transverse |
0.425 % (Max.) 0.625 % (Max.) |
0.30 0.45 |
NA NA |
NA NA |
| Resistance to impact by small diameter ball | 20N (Min.) | >20 | 20N (Min.) | >20 |
| Resistance to cracking | Should pass test | Complies | Should pass test | Complies |
| Resistance to scratching | 2N (Min.) | >2 | 2.N (Min.) | >2 |
| Resistance to staining 1. Acetone 2. Coffee 3. Sodium Hydroxide – 25% Solution 4. Hydrogen Peroxide – 30% Solution 5. Shoe Polish 6. Citric Acid – 10% Solution |
5 5 5 4 4 4 |
5 5 5 4 4 4 |
Should pass test | Complies |
| Resistance to colour change 1. In Xenon light 2. In Enclosed Carbon ARC light |
Wool Standard 6 5 |
6 5 |
Wool Standard Should pass test Should pass test |
Complies Complies |
| Resistance to cigarette burns | 3 | 3 | Should pass test | Complies |
| Resistance to steam | 4 | 4 | Should pass test | Complies |
| Appearance | Free from surface defects | Complies | No ABC Defects | No ABC Defects |
| Specific gravity gm/cm3 | NA | 1.36 (Min.) | NA | 1.40 (Min.) |